Cast Aluminium Column

Product Name: Cast Aluminum Column
Material: ZL101A
Casting Weight: 2.8KG
Casting Process: Sand Casting
Standards: ASTM,AISI,DIN,BS,JIS
Chat Now

Product Details

Product NameCasting ProcessStandardsProductionMaterial

Cast Aluminum Column

Sand CastingASTM,AISI,DIN,BS,JIS100000 Pieces

ZL101A

Dimension 

Tolerance

 Surface RoughnessCasting WeightManufactureSurface treatment
CT8Ra6.3-122.8KGOEM/ODMMill finished, anodizing, powder coating, brushing, polishing


Payment & Shipping Terms:

Minimum Order  Quantity100
Price$1-500
Delivery Time4 weeks
Payment TermsT/T, LC
Packaging DetailsCarton and Wood









Youtubehttps://www.youtube.com/watch?v=Z9V7uZi9rZE 




Introduction of Cast Aluminium Column:

When smelting, the order and method of loading the material into the furnace are not only related to the melting time, the burning loss of metal and the heat energy consumption, but also to the quality of metal melt and the service life of furnace. The loading principles include:

1. The charging sequence shall be reasonable. The correct charge shall be determined according to the nature and condition of the added charge, and shall also take into account the fastest melting speed, the least burning loss and the accurate chemical composition control.

When loading, first load small pieces or sheet scrap, aluminum ingots and bulk materials in the middle, and finally install the intermediate alloy. The intermediate alloy with melting point and easy oxidation is installed in the middle and lower layer. The loaded furnace materials shall be uniformly distributed in the molten pool to prevent bias.

Small pieces or sheet materials are installed in the lower layer of the molten pool, which can reduce the burning loss and protect the furnace body from the direct impact of large pieces of material. Intermediate alloy from high melting point, such as AL, NI and AL - MN alloy melting point is 750-800 ℃, installed in the upper, because the upper furnace high temperature easy to melt, there are also plenty of time to spread; The uniform distribution of the intermediate alloy is beneficial to the composition control of the melt.

The charge is flat and the melting speed is similar everywhere to prevent the partial metal from overheating when the weight is too heavy.

The charge shall be put into the furnace once, and the second or more charges will increase the amount of non-metal inclusion and gas content.